C 3660-408:2019 (IEC 60811-408:2012) 

(1) 

目 次 

ページ 

序文 ··································································································································· 1 

1 適用範囲························································································································· 1 

2 引用規格························································································································· 1 

3 用語及び定義 ··················································································································· 2 

4 試験方法························································································································· 2 

4.1 非充塡形ケーブルの試験方法 ··························································································· 2 

4.2 充塡形ケーブルの試験方法 ······························································································ 3 

5 試験報告書 ······················································································································ 4 

附属書A(規定)試料の調整 ·································································································· 5 

C 3660-408:2019 (IEC 60811-408:2012) 

(2) 

まえがき 

この規格は,産業標準化法第12条第1項の規定に基づき,一般社団法人日本電線工業会(JCMA)及び

一般財団法人日本規格協会(JSA)から,産業標準原案を添えて日本産業規格を制定すべきとの申出があ

り,日本産業標準調査会の審議を経て,経済産業大臣が制定した日本産業規格である。これによって,JIS 

C 3660-4-2:2011は廃止され,その一部を分割して制定したこの規格に置き換えられた。 

この規格は,著作権法で保護対象となっている著作物である。 

この規格の一部が,特許権,出願公開後の特許出願又は実用新案権に抵触する可能性があることに注意

を喚起する。経済産業大臣及び日本産業標準調査会は,このような特許権,出願公開後の特許出願及び実

用新案権に関わる確認について,責任はもたない。 

JIS C 3660の規格群には,次に示す部編成がある。 

JIS C 3660-100 第100部:一般事項 

JIS C 3660-201 第201部:一般試験−絶縁体厚さの測定 

JIS C 3660-202 第202部:一般試験−非金属シース厚さの測定 

JIS C 3660-203 第203部:一般試験−仕上寸法の測定 

JIS C 3660-301 第301部:電気試験−充塡コンパウンドの23 ℃における誘電率の測定 

JIS C 3660-302 第302部:電気試験−充塡コンパウンドの23 ℃及び100 ℃における直流抵抗率の測

定 

JIS C 3660-401 第401部:各種試験−加熱老化試験方法−エアオーブンによる加熱老化 

JIS C 3660-402 第402部:各種試験−耐水性試験 

JIS C 3660-403 第403部:各種試験−架橋コンパウンドのオゾン試験 

JIS C 3660-404 第404部:各種試験−シースの耐油試験 

JIS C 3660-405 第405部:各種試験−PVC絶縁体及びPVCシース材料の熱安定性試験 

JIS C 3660-406 第406部:各種試験−ポリエチレン及びポリプロピレンコンパウンドの耐環境応力亀

裂性試験 

JIS C 3660-407 第407部:各種試験−ポリエチレン及びポリプロピレンコンパウンドの質量増加率 

JIS C 3660-408 第408部:各種試験−ポリエチレン及びポリプロピレンコンパウンドの長期安定性試

験 

JIS C 3660-409 第409部:各種試験−熱可塑性絶縁体及びシース材料の加熱減量試験 

JIS C 3660-410 第410部:各種試験−銅導体を被覆するポリオレフィン絶縁材料の銅触媒による酸化

劣化試験 

JIS C 3660-411 第411部:各種試験−充塡コンパウンドの低温ぜい化 

JIS C 3660-412 第412部:各種試験−加熱老化試験方法−加圧空気による加熱老化 

JIS C 3660-501 第501部:機械試験−絶縁体及びシース用コンパウンドの機械的特性試験 

JIS C 3660-502 第502部:機械試験−絶縁体の収縮試験 

JIS C 3660-503 第503部:機械試験−シースの収縮試験 

JIS C 3660-504 第504部:機械試験−絶縁体及びシースの低温曲げ試験 

JIS C 3660-505 第505部:機械試験−絶縁体及びシースの低温伸び試験 

C 3660-408:2019 (IEC 60811-408:2012) 

(3) 

JIS C 3660-506 第506部:機械試験−絶縁体及びシースの低温衝撃試験 

JIS C 3660-507 第507部:機械試験−架橋した材料のホットセット試験 

JIS C 3660-508 第508部:機械試験−絶縁体及びシースの加熱変形試験 

JIS C 3660-509 第509部:機械試験−絶縁体及びシースの巻付加熱試験 

JIS C 3660-510 第510部:機械試験−ポリエチレン及びポリプロピレンコンパウンドの試験方法−加

熱による前処理後の巻付試験 

JIS C 3660-511 第511部:機械試験−ポリエチレン及びポリプロピレンコンパウンドのメルトフロー

インデックスの測定 

JIS C 3660-512 第512部:機械試験−ポリエチレン及びポリプロピレンコンパウンドの試験方法−加

熱による前処理後の引張強さ及び破断時の伸び試験 

JIS C 3660-513 第513部:機械試験−ポリエチレン及びポリプロピレンコンパウンドの試験方法−前

処理後の巻付試験 

JIS C 3660-601 第601部:物理試験−充塡コンパウンドの滴下点の測定 

JIS C 3660-602 第602部:物理試験−充塡コンパウンドの油分離 

JIS C 3660-603 第603部:物理試験−充塡コンパウンドの全酸価の測定 

JIS C 3660-604 第604部:物理試験−充塡コンパウンド中の腐食成分試験 

JIS C 3660-605 第605部:物理試験−ポリエチレンコンパウンド中のカーボンブラック及び無機充塡

剤の含有量測定 

JIS C 3660-606 第606部:物理試験−密度測定法 

JIS C 3660-607 第607部:物理試験−ポリエチレン及びポリプロピレン中のカーボンブラック分散測

定方法 

  

日本産業規格          JIS 

C 3660-408:2019 

(IEC 60811-408:2012) 

電気・光ファイバケーブル− 

非金属材料の試験方法−第408部:各種試験− 

ポリエチレン及び 

ポリプロピレンコンパウンドの長期安定性試験 

Electric and optical fibre cables- 

Test methods for non-metallic materials-Part 408: Miscellaneous tests- 

Long-term stability test of polyethylene and polypropylene compounds 

序文 

この規格は,2012年に第1版として発行されたIEC 60811-408を基に,技術的内容を変更することなく

作成した日本産業規格である。 

なお,この規格で点線の下線を施してある参考事項は,対応国際規格にはない事項である。 

適用範囲 

この規格は,ケーブル構成材料であるポリエチレンコンパウンド及びポリプロピレンコンパウンドの品

質が通信ケーブルの推奨寿命を満足することを確認する手順について規定する。 

この試験は,選定した材料がケーブルの推奨寿命を満足することを確認するための材料選定試験として

だけ考慮されている。試験期間は,日常的な品質管理試験には適切ではない。材料の管理として適切な方

法の一つがJIS C 3660-410に規定されている。 

注記 この規格の対応国際規格及びその対応の程度を表す記号を,次に示す。 

IEC 60811-408:2012,Electric and optical fibre cables−Test methods for non-metallic materials−Part 

408: Miscellaneous tests−Long-term stability test of polyethylene and polypropylene compounds

(IDT) 

なお,対応の程度を表す記号“IDT”は,ISO/IEC Guide 21-1に基づき,“一致している”こ

とを示す。 

引用規格 

次に掲げる規格は,この規格に引用されることによって,この規格の規定の一部を構成する。これらの

引用規格は,その最新版(追補を含む。)を適用する。 

JIS C 3660-100 電気・光ファイバケーブル−非金属材料の試験方法−第100部:一般事項 

注記 対応国際規格:IEC 60811-100:2012,Electric and optical fibre cables−Test methods for 

non-metallic materials−Part 100: General 

C 3660-408:2019 (IEC 60811-408:2012) 

  

JIS C 3660-410 電気・光ファイバケーブル−非金属材料の試験方法−第410部:各種試験−銅導体を

被覆するポリオレフィン絶縁材料の銅触媒による酸化劣化試験 

注記 対応国際規格:IEC 60811-410,Electric and optical fibre cables−Test methods for non-metallic 

materials−Part 410: Miscellaneous tests−Test method for copper-catalyzed oxidative degradation of 

polyolefin insulated conductors 

JIS K 6257 加硫ゴム及び熱可塑性ゴム−熱老化特性の求め方 

注記 対応国際規格:ISO 188,Rubber, vulcanized or thermoplastic−Accelerated ageing and heat 

resistance tests 

用語及び定義 

この規格で用いる主な用語及び定義は,JIS C 3660-100の箇条3による。 

試験方法 

4.1 

非充塡形ケーブルの試験方法 

4.1.1 

一般 

この規格は,JIS C 3660-100と併せて用いる。 

注記 この試験は,銅線対をもつ通信用ケーブルを対象としており,配電用ケーブルについては,試

験方法を検討中である。 

ケーブル構成材料の品質が,ケーブル推奨寿命を超えるかどうかの確認が必要となる場合がある。 

特に,ポリオレフィン絶縁体は,商用においても高い寿命を保有しなければならない。 

試験期間の定義,温度,環境及び破壊の判定基準は,注意して選択する。 

試験温度及び試験期間については,関連ケーブル規格に規定されたケーブルシステム条件の厳しさに従

って,次のいずれかの試験条件を用いる。 

条件A:100 ℃で42日間。 

直接埋設するケーブル,ダクト若しくはトラフの中に布設するケーブル,又は温暖な気候の

下で地上に露出した状態に布設するケーブルのように,通常50 ℃未満の過酷過ぎない条件下

で使用するケーブルの絶縁体に適用する。 

条件B:105 ℃で42日間。 

キャビネット,ターミナルボックスのような,地上の高温条件下に布設するケーブルの絶縁

体に適用する。 

4.1.2 

装置 

この試験で用いる装置は,次による。 

a) 一般的にJIS K 6257に基づき,かつ,次の基準に適合するエアオーブン。 

− 試験中の平均温度は,規定値の±0.5 ℃以内で制御しなければならない 

− 試験中の温度の最大変動は,規定値の±1.0 ℃以下でなければならない。 

− 空気の置換:1時間当たり6回以上の換気。疑義がある場合には,1時間当たり最大10回とする。 

代わりに,1室以上の隔室からなる,次の寸法をもつ,上記の基準を満たす試験装置を使用しても

よい。 

隔室高さ:250 mm以上 

隔室径:75 mm以上 

C 3660-408:2019 (IEC 60811-408:2012) 

高さと径との比:3:1〜4:1 

注記 [対応国際規格の注記の内容は,規定であることから,細別a) の第2段落とした。] 

b) a) のエアオーブンの体積に対して,適切な計測範囲を備えた空気流量計。 

c) 0.1 ℃単位で読取り可能であり,測定誤差が0.2 ℃以下の熱電対又は温度計。 

d) 精度が±0.5 mgで0.1 mgの読取り及び繰返し測定可能な化学天びん(秤)。 

4.1.3 

試料及び試験片の準備 

非充塡形ケーブルから,2 mの試料を各色について三つの試料を採取する。これらの試料は,附属書A

に規定された試験を実施した後,A.4の要求事項を満足しなければならない。 

試料から200 mmの試料を3本以上,上記の試験を実施した試料から切断し採取する。これらは,試料

の端から等間隔に200 mmずつ切る。 

各試料について,亀裂及び割れのないことを確認しながら,手で隙間なく10回の自己巻付処理を行う。 

4.1.4 

加熱方法 

巻付けを行った試料を60±2 ℃の空気循環式エアオーブンに7日間放置する。 

4.1.5 

結果の評価 

加熱処理期間の終了後,目視によって,亀裂及び割れのないことを確認する。 

4.2 

充塡形ケーブルの試験方法 

4.2.1 

一般 

一般事項は,4.1.1による。 

充塡コンパウンド入りのポリオレフィン絶縁ケーブルでは,絶縁体と充塡材との組合せ適合性を評価す

る。 

4.2.2 

装置 

装置は,4.1.2による。 

4.2.3 

試料及び試験片の準備 

2.5 mの長さで採取した各色三つの試料を,充塡コンパウンド中で,次の温度で7日間前処理を行う。 

− 60±2 ℃(滴下点温度が50 ℃を超え70 ℃以下の充塡コンパウンドの場合) 

− 70±2 ℃(滴下点温度が70 ℃を超える充塡コンパウンドの場合) 

注記 滴下点については,JIS C 3660-601を参照。 

絶縁線心又はケーブルをガラス容器に入れた約200 gの充塡コンパウンドへ浸せきする(両端は浸せき

しない。)ことによって前処理を行う。ケーブルを用いる場合は,前処理後の試験片採取に注意を払う。 

前処理後,試料をけばのない吸取紙で余分な充塡コンパウンドを拭き取る。充塡コンパウンドに浸せき

した中央部を残して両端を切り落とし,各色三つの試料を2 mの長さに切る。これらの試料は,附属書A

に規定された試験を実施した後,A.4の要求事項を満足しなければならない。 

その後,各試料から200 mmの試料を3本以上,上記の試験を実施した試料から切断し採取する。これ

らは,試料の端から等間隔に200 mmずつ切る。各試料の亀裂及び割れのないことを確認しながら,手で

隙間なく10回の自己巻付処理を行う。 

4.2.4 

加熱手順 

加熱手順は,4.1.4による。 

4.2.5 

結果の評価 

結果の評価は,4.1.5による。 

C 3660-408:2019 (IEC 60811-408:2012) 

  

試験報告書 

試験報告書は,JIS C 3660-100に従って作成する。 

C 3660-408:2019 (IEC 60811-408:2012) 

附属書A 

(規定) 

試料の調整 

A.1 試験片の準備 

三つの試料をそれぞれ別々に約60 mm径の緩いコイル状に巻く。試験片には,よじれ又はねじれがあっ

てはならない。必要ならば,コイルを2本のアルミニウム線で緩く縛ってもよい。各試料の質量を0.1 mg

単位で計量する。 

A.2 加熱手順 

三つの試料は,蓋に取り付けたアルミニウム線のフックなどによってエアオーブンの下部につるす。試

料のコイル中心の空気温度が,条件A又は条件Bによって規定する温度で維持されているか確認するため

に熱電対又は適切な温度計で計測する(4.1.1参照。)。 

試験装置が隔室を備えている場合,各試料は,それぞれ違う隔室に入れることが望ましい。ただし,試

料は三つまでを一つの隔室内で老化してもよい。この場合,互いの試料又は内壁に触れないように,3〜5 

mm離してつるす。 

試験中の温度を監視するために,データ記録装置を使用することが望ましい。 

規定する試験期間の後,試料をエアオーブンから取り出し,常温まで冷却する。 

注記 (対応国際規格の注記の内容は,規定であることから,この箇条の第3段落とした。) 

A.3 測定 

熱処理後,各試料の質量を0.1 mg単位で測定する。 

A.4 結果の評価 

目視で絶縁体の亀裂,割れ,劣化などの兆候があってはならず,かつ,色は識別可能でなければならな

い。 

質量の増加を計算し,これが1 mgを超えてはならない。又は,JIS C 3660-410の酸化誘導時間の試験を

行ったとき,2分以上の誘導時間でなければならない。